Stainless Steel electrode
Stainless Steel Welding Electrode HT-A102
In accordance with: GB E308-16
Equivalent: AWS E308-16
Stainless Steel Welding Electrode
Instruction: HT-A102 is lime titania type coating stainless steel electrode, its weld metal has good mechanical properties and resistance to intercrystalline corrosion. This type electrode takes foreign advanced technology, its coating shows red, be suitable for AC&DC+, and ACs arc will have a better stability. It also has excellent welding performance such as soft arc, small & little splash, good welding seam and the capability for allposition welding work.
Application: Be suitable for the corrosionresisting 0Cr18Ni9, Cr18Ni9Ti stainless steel structure with the working temperature lower than 300.
Chemical composition of deposited metal(%)
C | Mn | Si | Cr | Ni | Mo | Cu | S | P |
≤ 0.08 |
0.52.5 | ≤ 0.90 |
18.021.0 |
9.011.0 | ≤ 0.75 | ≤ 0.75 | ≤ 0.030 | ≤ 0.040 |
Mechanical Properties of deposited metal:
Tensile Strength (MPa) | Elongation A(%) |
≥ 550 | ≥ 35 |
Referenced Current: (AC/ DC+)
Diameter(mm) | 2.0 | 2.5 | 3.2 | 4.0 | 5.0 | |
Length(mm) | 300 | 300 | 350 | 400 | 400 | |
Current (A) Scope | Flat weld | 3050 | 6085 | 85120 | 115150 | 140180 |
Vertical up weld | 3050 | 5070 | 75105 | 95130 |
|
Notice:
1. Before welding, the electrode should be dried for 1 hour at 250300.
2. Try best to use low current and short arc when welding, and the amplitude of swing shall be no more than two and a half of the diameter size.
3. Before welding, the inclusion such as oil, rust, water, etc must be cleared from the weldment.